点击图片查看大图PVC增韧改质剂K-71在透明片材中的应用
Summary of K-71
PVC增韧改质剂K-71简介
1. Improvement of Impact Strength
提高冲剂强度
√K-71 improved almost 3%~5% at impact strength
√K-71提升3%~5%的冲击强度（原配方）。
2. Improvement of Fish Eye characteristics
晶点的改善
√ K-71 improved fish eye characteristic,
改善晶点
it can help to manufacture better
surface quality transparency sheet.
提升透明片材的表面性能
3. Other physical properties and
processing are almost same.
物理性能及加工性能
√ Easy processing
加工更容易
√ Improvement thermal stability
改善热稳定性
Comparison of processing
PVC增韧改质剂K-71性能比较
K-71 is added Formulations，it has easy processing because of better lubrication ability.
添加了K-71的配方具有更好的加工流变性能。
Fusion Behavior(塑化情况)
|
Grade
|
F/Time(sec)塑化
|
F/Torque(N.m)塑化扭矩
|
E/Torque(N.m)平衡扭矩
|
|
NA
|
59
|
36
|
17.6
|
|
K-71
|
52
|
36.2
|
16.5
|
Test Condition（测试条件）1. Machine : T（设备）hermo Haake PolyDrive（哈克流变仪）
2. Mixer Temp（温度设定）: 155 ℃ / Rotor speed （转速）: 70 rpm / Charge Weight （投料量）: 56 g
3. SQ Comp’d + MBS 7 PHR（添加7phr的MBS）
Comparison of physical & Optical Property
PVC增韧改质剂K-71物理性能及透明性比较
|
TEST Items
|
unit
|
K-71
|
Non
|
|
|
MBS
|
8phr
|
Non break ratio
|
70
|
63
|
|
Crease Whitening
|
Haze
|
15.6
|
16.7
|
|
|
Transparency(3mm press)
|
Tt
|
75.3
|
70.5
|
|
|
Haze
|
4.3
|
4.6
|
||
|
Fish eye
|
5 scale
|
4.0
|
6.0
|
|
Test Condition（测试条件）1. Machine : Rotary Impact Tester 设备：旋转式冲击试验机
2. Test Temp.测试温度 : Room Temperature室温 (23 ℃)
3. Rotary Impact Strength 旋转冲击强度: 6phr: 1,000rpm X 15sec, 8phr: 1,060rpm X 15sec
4. Roll-mill press压片 : 195℃ _ 185℃ pressed压。