性能项目
|
测试条件
|
测试方法
|
数值/描述
|
单位
|
||||||
机械性能
|
拉伸强度(引张强度)
|
ASTM D638/ISO 527
|
294
|
kg/cm²(MPa)[Lb/in2]
|
||||||
断裂伸长率
|
ASTM D638/ISO 527
|
500
|
%
|
|||||||
拉伸模量
|
ASTM D638/ISO 527
|
12800
|
kg/cm²(MPa)[Lb/in2]
|
|||||||
拉伸屈服伸长率(延伸率)
|
ASTM D638/ISO 527
|
%
|
||||||||
拉伸断裂伸长率(延伸率)
|
ASTM D638/ISO 527
|
%
|
||||||||
弯曲模量(弯曲弹性率)
|
ASTM D790/ISO 178
|
kg/cm²(MPa)[Lb/in2]
|
||||||||
弯曲强度
|
ASTM D790/ISO 178
|
kg/cm²(MPa)[Lb/in2]
|
||||||||
洛氏硬度
|
ASTM D785
|
90
|
kg·cm/cm(J/M)ft·lb/in
|
|||||||
IZOD 缺口冲击强度
|
1/4" 23℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
|||||||
1/4" -30℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||||||||
1/8" 23℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||||||||
1/8" -30℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||||||||
Charpy冲击强度
|
23℃ (缺口)
|
ASTM D256/ISO 179
|
53.9
|
kg·cm/cm(J/M)ft·lb/in
|
||||||
-30℃(缺口)
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||||||||
23℃(无缺口)
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||||||||
-30℃(无缺口)
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||||||||
物性性能
|
比重(密度)
|
ASTM D792/ISO 1183
|
0.900
|
|||||||
成型收缩率
|
ASTM D955
|
%
|
||||||||
熔融指数(流动系数)
|
200℃/5kg
|
ASTM D1238/ISO 1133
|
20
|
g/10min
|
||||||
220℃/10kg
|
ASTM D1238/ISO 1133
|
g/10min
|
||||||||
吸水率 23℃/24H
|
ASTM D570/ISO 62
|
%
|
||||||||
热性能
|
热变形温度
|
退火
|
ASTM D648/ISO 75
|
℃(℉)
|
||||||
未退火
|
ASTM D648/ISO 75
|
88
|
℃(℉)
|
|||||||
维卡软化点
|
ASTM D1525/ISO R306
|
135
|
℃(℉)
|
|||||||
熔点
|
-
|
℃(℉)
|
||||||||
燃烧性(率)
|
UL94
|
|||||||||
线性膨胀系数
|
ASTM D696/ISO 11359
|
mm/mm.℃
|
||||||||
加工条件
|
干燥条件
|
|||||||||
加工温度
|
射嘴
|
℃
|
||||||||
料筒前段
|
℃
|
|||||||||
料筒中段
|
℃
|
|||||||||
料筒后段
|
℃
|
|||||||||
熔体温度
|
℃
|
|||||||||
模具温度
|
℃
|
|||||||||
压力
|
注塑压力
|
Mpa
|
||||||||
保压压力
|
Mpa
|
|||||||||
背压
|
Mpa
|
|||||||||
螺杆转速
|
rpm
|
|||||||||
其他
|
备注
|
|||||||||
颜色
|
||||||||||
特性
|
抗撞击性良好
|
|||||||||
用途
|
食品容器,医疗器械
|
供应 韩国LG化学 R6400 医疗级PP