性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | kg/cm2(MPa)[Lb/in2] | ||
断裂伸长率 | ASTM D638/ISO 527 | 40 | % | ||
拉伸模量 | ASTM D638/ISO 527 | 3300 | kg/cm2(MPa)[Lb/in2] | ||
拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | % | |||
拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 3000 | kg/cm2(MPa)[Lb/in2] | ||
弯曲强度 | ASTM D790/ISO 178 | kg/cm2(MPa)[Lb/in2] | |||
洛氏硬度 | ASTM D955 | ||||
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
-30℃(缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
23℃(无缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
-30℃(无缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
物性性能 | 比重(密度) | ASTM D792/ISO 1183 | 1.18 | ||
成型收缩率 | ASTM D955 | % | |||
熔融指数(流动系数) | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | ||
220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
吸水率 23℃/24H | ASTM D570/ISO 62 | % | |||
热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | ℃(℉) | |
未退火 | ASTM D648/ISO 75 | ℃(℉) | |||
维卡软化点 | ASTM D1525/ISO R306 | ℃(℉) | |||
熔点 | - | ℃(℉) | |||
燃烧性(率) | UL94 | V-2 | |||
线性膨胀系数 | ASTM D696/ISO 11359 | mm/mm.℃ | |||
电气性能 | 介电常数 | 100HZ | ASTM D150/IEC 60250 | ||
1MHZ | ASTM D150/IEC 60250 | ||||
体积电阻率 | ASTM D257/IEC 60093 | Ω.cm | |||
表面电阻率 | ASTM D257/IEC 60093 | Ω | |||
耐电弧性 | ASTM D495/IEC 60112 |
|