| 所有数据一般信息物理性能力学性能热性能电气性能与可燃性其它加工信息 | 单位 英制 | 公制 |
| 产品说明 | ||||
|
VALOX 4012G is a 10% glass fibre reinforced PBT injection moulding resin with excellent mechanical properties. Applications: connectors. This grade is a 4012 with improved cycle time and ductility.
|
||||
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
填料/增强材料
|
|
|||
|
性能特点
|
|
|||
|
用途
|
|
|||
|
RoHS 合规性
|
|
|||
|
加工方法
|
|
|||
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.35
|
g/cm³
|
ASTM D792, ISO 1183 |
|
熔流率
|
ASTM D1238 | ||
|
250°C/1.2 kg
|
10
|
g/10 min
|
|
|
266°C/5.0 kg
|
90
|
g/10 min
|
|
|
溶化体积流率（MVR）
|
ISO 1133 | ||
|
250°C/1.2 kg
|
9.00
|
cm³/10min
|
|
|
250°C/5.0 kg
|
50.0
|
cm³/10min
|
|
|
265°C/5.0 kg
|
80.0
|
cm³/10min
|
|
|
收缩率
|
Internal Method | ||
|
流动 2
|
0.60 到 0.90
|
%
|
|
|
流动: 3.20 mm
|
0.60 到 1.6
|
%
|
|
|
横向流动 2
|
0.70 到 1.0
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.20
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.070
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (R 计秤)
|
120
|
ISO 2039-2 | |
|
球压硬度 (H 358/30)
|
110
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 3
|
4400
|
MPa
|
ASTM D638 |
|
--
|
4500
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 4
|
80.0
|
MPa
|
ASTM D638 |
|
屈服
|
80.0
|
MPa
|
ISO 527-2/5 |
|
断裂 4
|
80.0
|
MPa
|
ASTM D638 |
|
断裂
|
80.0
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 4
|
3.0
|
%
|
ASTM D638 |
|
屈服
|
3.0
|
%
|
ISO 527-2/5 |
|
断裂 4
|
3.0
|
%
|
ASTM D638 |
|
断裂
|
3.0
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 5
|
3800
|
MPa
|
ASTM D790 |
|
-- 6
|
3800
|
MPa
|
ISO 178 |
|
弯曲强度
|
|||
|
-- 6, 7
|
120
|
MPa
|
ISO 178 |
|
-- 6, 8
|
125
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 5
|
120
|
MPa
|
ASTM D790 |
|
断裂, 50.0 mm 跨距 5
|
120
|
MPa
|
ASTM D790 |
|
断裂抗挠强度 9
|
5.0
|
%
|
ISO 178 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
|||
|
-30°C 10
|
6.0
|
kJ/m²
|
ISO 179/1eA, ISO 179/2C |
|
23°C 10
|
7.0
|
kJ/m²
|
ISO 179/1eA |
|
23°C
|
6.0
|
kJ/m²
|
ISO 179/2C |
|
简支梁缺口冲击强度
|
|||
|
-30°C 10
|
45
|
kJ/m²
|
ISO 179/1eU |
|
-30°C
|
33
|
kJ/m²
|
ISO 179/2U |
|
23°C 10
|
45
|
kJ/m²
|
ISO 179/1eU |
|
23°C
|
33
|
kJ/m²
|
ISO 179/2U |
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
50
|
J/m
|
ASTM D256 |
|
0°C
|
50
|
J/m
|
ASTM D256 |
|
23°C
|
50
|
J/m
|
ASTM D256 |
|
-30°C 11
|
5.0
|
kJ/m²
|
ISO 180/1A |
|
0°C 11
|
5.0
|
kJ/m²
|
ISO 180/1A |
|
23°C 11
|
5.0
|
kJ/m²
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
-30°C
|
380
|
J/m
|
ASTM D4812 |
|
23°C
|
380
|
J/m
|
ASTM D4812 |
|
-30°C 11
|
30
|
kJ/m²
|
ISO 180/1U |
|
23°C 11
|
35
|
kJ/m²
|
ISO 180/1U |
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
4.00
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
215
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 100 mm 跨距 12
|
215
|
°C
|
ISO 75-2/Be |
|
0.45 MPa, 未退火, 64.0 mm 跨距 13
|
215
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
190
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 100 mm 跨距 12
|
170
|
°C
|
ISO 75-2/Ae |
|
1.8 MPa, 未退火, 64.0 mm 跨距 13
|
185
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
220
|
°C
|
ASTM D1525 14, ISO 306/A50 14 |
|
--
|
205
|
°C
|
ASTM D1525 15, ISO 306/B50 15 |
|
--
|
200
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (125°C)
|
Pass
|
IEC 60695-10-2 | |
|
线形膨胀系数
|
|||
|
流动: -40 到 40°C
|
0.000060
|
cm/cm/°C
|
ASTM E831 |
|
流动: -40 到 40°C
|
0.000046
|
cm/cm/°C
|
ISO 11359-2 |
|
流动: 23 到 80°C
|
0.000060
|
cm/cm/°C
|
ISO 11359-2 |
|
流动: 23 到 150°C
|
0.000048
|
cm/cm/°C
|
ISO 11359-2 |
|
横向: -40 到 40°C
|
0.000080
|
cm/cm/°C
|
ASTM E831 |
|
横向: -40 到 40°C
|
0.000082
|
cm/cm/°C
|
ISO 11359-2 |
|
横向: 23 到 80°C
|
0.000080
|
cm/cm/°C
|
ISO 11359-2 |
|
横向: 23 到 150°C
|
0.00021
|
cm/cm/°C
|
ISO 11359-2 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.0E+15
|
ohm
|
IEC 60093 |
|
体积电阻率
|
> 1.0E+15
|
ohm·cm
|
ASTM D257, IEC 60093 |
|
介电强度
|
|||
|
0.800 mm, in Oil
|
30
|
kV/mm
|
ASTM D149 |
|
1.60 mm, in Oil
|
23
|
kV/mm
|
ASTM D149 |
|
3.20 mm, in Oil
|
18
|
kV/mm
|
ASTM D149 |
|
0.800 mm, 在油中
|
30
|
kV/mm
|
IEC 60243-1 |
|
1.60 mm, 在油中
|
23
|
kV/mm
|
IEC 60243-1 |
|
3.20 mm, 在油中
|
18
|
kV/mm
|
IEC 60243-1 |
|
介电常数
|
|||
|
1 MHz
|
3.40
|
ASTM D150, IEC 60250 | |
|
50 Hz
|
3.10
|
IEC 60250 | |
|
60 Hz
|
3.10
|
IEC 60250 | |
|
耗散因数
|
|||
|
1 MHz
|
0.015
|
ASTM D150, IEC 60250 | |
|
50 Hz
|
0.0010
|
IEC 60250 | |
|
60 Hz
|
0.0010
|
IEC 60250 | |
|
漏电起痕指数
|
IEC 60112 | ||
|
--
|
325
|
V
|
|
|
解决方案 B
|
150
|
V
|
|
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.60 mm, Testing by SABIC)
|
HB
|
UL 94 | |
|
灼热丝易燃指数 (1.00 mm)
|
750
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度
|
IEC 60695-2-13 | ||
|
1.00 mm
|
775
|
°C
|
|
|
1.50 mm
|
800
|
°C
|
|
|
2.00 mm
|
775
|
°C
|
|
|
3.00 mm
|
750
|
°C
|
| 如需查询更多产品信息，请前往公司主营网站http://qianqiuguoji.1688.com | |
| 联系人: | 李正强经理 |
| 联系手机: | 15335258581 |
| 公司电话: | 0512-86895007 |
| 客服Q Q: | 2078002886 |
| 邮箱: | 2078002886@qq.com |
| 传真: | 0512-86895003（请注明李正强经理收） |