点击图片查看大图
厂家(产地)：日本东丽 牌号：700 加工级别：注塑级
用途级别：通用级 销售方式：品牌经销 类型：标准料
规格级别：通用
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 熔体流动速率 | 220℃ 10kg | ISO-1133 | 23 | g/10min | |
| 比重 | 23℃ | ASTM D-792 | 1.05 | |||
| 模塑收缩率 | ASTM D-955 | 0.4-0.6 | % | |||
| 体积阻力 | 23℃ | ASTM D-257 | ＞1016 | ohm.cm | ||
| 阻燃性 | UL-94 | HB | ||||
| 吸水性 | 23℃×24hrs | ASTM D-570 | 0.3 | % | ||
| 表面阻力 | 23℃ | ASTM D-257 | ＞1016 | ohm | ||
| 机械性能 | 拉伸断裂伸长率 | 23℃ | ASTM D-638 | 35 | % | |
| 弯曲模量 | 23℃ | ASTM D-790 | 25000(2450) | kg/cm2(MPa) | ||
| IZOD冲击强度 | 12.7×62.5×12.7mm | 0℃ | ASTM D-256 | 11(108) | kg.cm/cm(J/m) | |
| 12.7×62.5×3.2mm | 0℃ | ASTM D-256 | 16(157) | kg.cm/cm(J/m) | ||
| IZOD冲击强度 | 12.7×62.5×12.7mm | 23℃ | ASTM D-256 | 19(186) | kg.cm/cm(J/m) | |
| 12.7×62.5×3.2mm | 23℃ | ASTM D-256 | 20(196) | kg.cm/cm(J/m) | ||
| 洛氏硬度 | ASTM D-785 | 115 | R | |||
| 弯曲强度 | 23℃(strainrate:3%) | ASTM D-790 | 770(76) | kg/cm2(MPa) | ||
| IZOD冲击强度 | 12.7×62.5×12.7mm | -30℃ | ASTM D-256 | 8(78) | kg.cm/cm(J/m) | |
| 12.7×62.5×3.2mm | -30℃ | ASTM D-256 | 12(118) | kg.cm/cm(J/m) | ||
| 拉伸强度 | 23℃(strainrate:5%) | ASTM D-638 | 510(50) | kg/cm2(MPa) | ||
| 电气性能 | 绝缘强度 | Short time | ASTM D-194 | 23 | KV/mm | |
| 电力因数 | 1000Hz | ASTM D-150 | 6.1×10-3 | |||
| 介电常数 | 1000Hz | ASTM D-150 | 3.1 | |||
| 热性能 | 热传导性能 | ASTM C177 | 0.15 | W/K.m | ||
| 线性膨胀系数 | ASTM D-696 | 7.1×10-5 | mm/mm℃ | |||
| 热变形温度 | 127×12.7×12.7mm | 18.56kg/cm2 | ASTM D-648 | 92 | ℃ | |
| 127×12.7×6.4mm | 18.56kg/cm2 | ASTM D-648 | 87 | ℃ | ||