点击图片查看大图供应日本三菱POM F25-03 高刚性耐磨
| 操作 |
牌号
|
熔融体积流量（MVR） (cm3/10min) | 简支梁缺口冲击强度 (kJ/m2) | 抗张强度 (MPa) | 拉伸断裂应变 (%) | 表面电阻率 (ohms) |
  
|
A10-03 | 2.2 (190°C/2.16 kg) | 8.0 (23°C) | 67.0 (屈服, ISO 527-1, -2) | 35 (50 mm/min) | 1.0E+16 |
|
|
A25-03 | 12 (190°C/2.16 kg) | 8.0 (23°C) | 69.0 (屈服, ISO 527-1, -2) | 35 (50 mm/min) | 1.0E+16 |
|
|
F10-01 | 2.2 (190°C/2.16 kg) | 8.0 (23°C) | 63.0 (屈服, ISO 527-1, -2) | 33 (50 mm/min) | 1.0E+16 |
|
|
F10-02 | 2.2 (190°C/2.16 kg) | 8.0 (23°C) | 63.0 (屈服, ISO 527-1, -2) | 33 (50 mm/min) | 1.0E+16 |
|
|
F10-EW | 3.4 (190°C/2.16 kg) | 8.0 (23°C) | 62.0 (屈服, ISO 527-1, -2) | 35 (50 mm/min) | |
|
|
F20-03 | 7.7 (190°C/2.16 kg) | 7.0 (23°C) | 64.0 (屈服, ISO 527-1, -2) | 30 (50 mm/min) | 1.0E+16 |
|
|
F20-05 | 7.7 (190°C/2.16 kg) | 7.0 (23°C) | 64.0 (屈服, ISO 527-1, -2) | 30 (50 mm/min) | 1.0E+16 |
|
|
F20-54 | 7.7 (190°C/2.16 kg) | 6.5 (23°C) | 62.0 (屈服, ISO 527-1, -2) | 30 (50 mm/min) | 1.0E+16 |
|
|
F20-61 | 7.7 (190°C/2.16 kg) | 6.0 (23°C) | 63.0 (屈服, ISO 527-1, -2) | 30 (50 mm/min) | 1.0E+13 |
|
F20-EW | 7.7 (190°C/2.16 kg) | 7.0 (23°C) | 64.0 (屈服, ISO 527-1, -2) | 30 (50 mm/min) | |
|
|
F25-03 | 14 (190°C/2.16 kg) | 6.5 (23°C) | 64.0 (屈服, ISO 527-1, -2) | 27 (50 mm/min) | 1.0E+16 |
|
|
F30-03 | 23 (190°C/2.16 kg) | 6.0 (23°C) | 64.0 (屈服, ISO 527-1, -2) | 25 (50 mm/min) | 1.0E+16 |
|
|
F30-05 | 23 (190°C/2.16 kg) | 6.0 (23°C) | 64.0 (屈服, ISO 527-1, -2) | 25 (50 mm/min) | 1.0E+16 |
|
|
F40-03 | 45 (190°C/2.16 kg) | 5.0 (23°C) | 64.0 (屈服, ISO 527-1, -2) | 20 (50 mm/min) | 1.0E+16 |
|
|
FRC-20 | 8.3 (190°C/2.16 kg) | 8.0 (23°C) | 57.0 (屈服, ISO 527-1, -2) | 42 (50 mm/min) | |
|
|
FV-30 | 27 (190°C/2.16 kg) | 6.0 (23°C) | 63.0 (屈服, ISO 527-1, -2) | 30 (50 mm/min) | 1.0E+13 |